離子浮選法處理電鍍廢水實驗研究
更新時間：2014-07-16 10:44
來源：環(huán)境工程學報
作者:
閱讀：2316
| 中文摘要: |
| 進行離子浮選法處理電鍍廢水的研究，對影響因素pH、CA∶CMe(摩爾比)、離子強度、浮選時間和通氣量等進行了實驗研究。實驗結果表明：離子分離選擇性遞減順序為：Cd2+>Zn2+>Fe2+ >Cu2+>Ni2+。當CA∶CMe為2.5～3∶1，pH為8.5～9，離子強度不高于0.0001 mol/L時，離子浮選對鎘、鋅、銅、鎳等金屬離子均有很高的去除率，Cd2+、Zn2+、Fe 2+、Ni 2+、Cu2+殘余濃度最低分別可達0.05、0.20、0.22、0.28和0.33 mg/L，處理后的電鍍廢水各污染物濃度均達到排放標準。泡沫產品中鎘、鋅、銅、鎳品位分別達到3.2％、9.3%、18.1%和13.2%，具有極高的資源回收價值。 |
| 英文摘要: |
| In this study, ion flotation method was used to dispose the electroplating wastewater. The effects of pH value, the ratio of CA∶CMe,ion strength, flotation time, volume of aeration on the treatment of the electroplating wastewater were studied. Experimental results showed that the decreasing order to separate the ions was Cd2+>Zn2+>Fe2+>Cu2+>Ni2+. The preferential segregation for the cadmium, zinc, copper, nickel was that the ratio of CA∶CMe was 2.5～3.1, pH value was 8.5～9, and the ion strength was less than 0.0001 mol/L. In this case, the residual concentrations of the Cd2+, Zn2+, Fe2+, Ni2+ and Cu2+ were 0.05, 0.20, 0.22,0.28 and 0.33 mg/L, respectively. After electroplating wastewater were disposed, the pollutant concentration complied with the discharge standard. The concentrations of the chromium, copper and nickel in the disposal froth product were 3.2％,9.3%,18.1% and 13.2%, respectively, which showed that there was a great reclamation value. |
聲明：轉載此文是出于傳遞更多信息之目的。若有來源標注錯誤或侵犯了您的合法權益，請作者持權屬證明與本網聯系，我們將及時更正、刪除，謝謝。
使用微信“掃一掃”功能添加“谷騰環(huán)保網”
如果需要了解更加詳細的內容，請點擊下載 
201407161044035682.zip
下載該附件請登錄，如果還不是本網會員，請先注冊